Yeah... My old team used to anodize. No problems with cracking, but re-welding anything was bad news. Are the cracks the result of powder coating + welding? Or is it just that the cracks are more visible due to the powder coating? Its kind of a dumb question, I know, but I don't think any of our anodized welds showed cracks (aside from a fall off a ramp in 2007).
|
The powder coat defiantly will make them more noticeable. The powder coating was not the cause of the crack.
A crack on the powder was a great indication that the weld COULD be a problem.
I am just saying that with the riveted solution, a cracked weld is NEVER a problem!