Quote:
Originally Posted by MattC9
Here's a nice tip that I have found out, .125 does not like to bend .090 likes to bend. So if you are planning to bend go .090 but if not go .125. We have a break and it did not like the 1/8th inch alum. we tried to bend the other day, it bent but not very well the .090 bends very well from what we have seen.
|
This will vary heavily based on the alloy.