Quote:
Originally Posted by FrankJ
At 2000 F your aluminum has turned into a puddle & no longer looks like a sprocket. Maybe even so at 1000F depending on the alloy. Anyway 1000 will have killed any age hardening.  |
Good catch, thanks! I got my metals mixed up, aluminum melts at ~1200F so disregard my previous comment.
-Adrian